Bag-ohay lang gipangutana kami kung ang usa ka strystal sa Occal wire naapektuhan sa proseso sa pag-antus nga hinungdanon kaayo ug dili malikayan nga proseso, ang among tubag dili. Here are some reasons.

In contrast, the process of drawing has a significant influence on the crystal morphology. If drawing is applied to single crystal copper, a short and thick crystal may be compressed into a long and slender one. Pananglitan, kung ang usa ka 8mm rod nadani sa usa ka gamay nga diameter sama sa pipila ka mga gatos sa usa ka milimetro, ang mga kristal mahimong makasinati sa pagkabahinbahin. In an extreme case, a single crystal could break into two, three, or more fragments depending on the drawing parameters. These parameters include the drawing speed and the ratio of the drawing dies. However, even after such fragmentation, the resulting crystals still maintain a columnar shape and continue to extend in a certain direction.

To sum up, annealing is a process that solely focuses on stress relief without modifying the number of single crystal copper crystals. It is drawing that can cause changes in crystal morphology and potentially lead to crystal fragmentation. Ang pagsabut sa kini nga mga kalainan hinungdanon alang sa husto nga pagdumala ug paggamit sa usa ka kristal nga materyales nga tumbaga nga tumbaga sa lainlaing mga aplikasyon sa industriya. Ang mga tiggama ug tigdukiduki kinahanglan nga hunahunaon ang angay nga mga pamaagi sa pagproseso pinasukad sa piho nga mga kinahanglanon sa mga produkto sa katapusan. Kung magpadayon ba ang integridad sa usa ka higpit nga istruktura sa kristal o aron makab-ot ang gitinguha nga porma sa kristal ug gidak-on, ang usa ka komprehensibo nga pagsabut sa pag-antus sa usa ka crystal c typer nga pagproseso sa materyal.